Combinatorial synthesis of oxide powders

H.M. Reichenbach and P.J. McGinn

Department of Chemical Engineering, University of Notre Dame, Notre Dame, Indiana 46556

(Received 31 July 2000; accepted 11 January 2001)

Combinatorial libraries of the mixed oxide system Cu

1−x

Ce

x

O

3

(0

艋 x 艋 1) have been

generated using a modified Pechini powder synthesis process in conjunction with

inkjet deposition. Mixed oxide crystalline powders were formed at temperatures below

500 °C. These powders have particle sizes in the range of 20.0 to 85.5 nm, and the

powder surface area increases with cerium content. In addition, each of the mixed

oxides (0 < x < 1) displayed catalytic activity in the CO oxidation reaction at

temperatures between 150 and 350 °C. This novel protocol has also been used to

generate a library of oxide powders of the perovskite-like La

1−x

Sr

x

CoO

3−

␦

system.

The La–Sr–Co–O system from this protocol exhibits lower average surface areas

than the Cu–Ce–O system (approximately 11.2 m

2

/g) due to higher decomposition

temperatures but still acts as an active catalyst for the CO oxidation reaction.