Combinatorial synthesis of oxide powders

D. X-ray diffraction

Using Cu

0.5

Ce

0.5

O

3

as a representative composition of

the mixed oxide library, powder x-ray diffraction was

performed on the decomposed powder from the solution-

phase synthesis copper ceria processed from Pechini

Method (CCP) and a powder made with traditional solid-

state processing techniques (CCS). The powder x-ray dif-

fraction patterns, in the 25° to 50° 2-

⍜ range, are shown

in Fig. 7. One of the CCPs was decomposed at 875 °C,

and the second was decomposed at 600 °C (which is the

standard decomposition temperature used in this study).

The solid-state cerium copper oxide powder was proc-

essed at 800 °C. The mixed oxide nature of the com-

pound is apparent, as the peaks of both CeO

2

(2-

⍜: 28.6°,

33.1°, and 47.2°) and CuO (2-

⍜: 35.5°, 38.7°, and 48.7°)

are present. The CCP decomposed at 875 °C is crystal-

line to the same degree as the CCS, and comparing the

two CCP powder patterns, there was no noticeable line

narrowing due to particle growth at the higher tempera-

ture. In addition to the crystalline nature of the mixed

oxide, the XRD pattern shows no obvious indication that

any organic residue from incomplete burnout of the resin

remains in either of the CCP powders. The degree of

crystallinity observed in the XRD patterns confirms that

600 °C was an optimal decomposition temperature for this

library of compounds.