Automotive Coatings Formulation: Chemistry, Physics und Practices

Electro deposition using two dipping steps
Since edge covering and throwing power of electro deposition primers were initially very poor and 
since electro powder coating and electro slurry coating failed to improve the throwing power, it 
was postulated that better results might be achieved by electro depositing two layers. After the first 
dipping step in a conventional electro deposition tank, the resulting primer layer was pre-gelled by 
stoving. The car body was then fed into a second dipping tank, where a second layer was applied. 
Those parts of the object which had been coated with just a thin layer in the first step exhibited a 
higher specific conductivity than the others. Those parts were preferentially coated in the second 
dipping step. The car body was then rinsed and both coating layers were stoved under the usual 
stoving conditions. The composition of the first tank met the demand for optimum corrosion resist-
ance, while the second tank conferred excellent flow and levelling to provide an optimum surface 
for the following topcoats 
[63]
. In the meantime, conventional electro deposition primers had been 
optimised to yield better edge covering, throwing power and levelling. It was therefore possible 
to forgo the two-step process, not least because it was very expensive to run two dipping tanks.
Nonionic electro deposition
Nonionically stabilised dispersions can be deposited at the cathode due to the formation of 
protons there from water. The resultant acids make the dispersion coagulate. If such systems 
do not contain volatile acids as neutralisation agents, it is possible to formulate with corrosion 
protection pigments, which would otherwise be diluted in aqueous phase under acidic condi-
tions, and to use metal pigments, e.g. zinc or aluminium, which are also sensitive to acids. This 
Automotive OEM coatings

---

55
renders any special pre-treatment unnecessary. Alternatively, such a process can be combined 
with a conventional electro deposition method 
[64]
.
Autophoresis
Colloidal solutions of polymer which develop acidity in aqueous phase (pH values of 2 to 3) can 
coagulate on the surface of metals. No electric field is needed for this. Coagulation occurs when 
the acid groups react with the metal atoms to form ions (salts) that are insoluble in water. The 
applied film layers are immobilized at relatively low stoving temperatures. Although this has not 
gained acceptance as a way of applying primers to entire car bodies, it is suitable for pre-coating 
metal parts for industrial uses and car accessories.