Automotive Coatings Formulation: Chemistry, Physics und Practices

Neutralisation agents
 
for anodic electro deposition primer resins are amines, e.g. triethylamine, 
N,N-dimethylethanolamine, diisopropanolamine, 2-amino-2-methyl-1-propanol (AMP). Since 
maleinised oils contain double bonds, they can undergo self-crosslinking, mainly at elevated 
temperatures in the presence of catalysts (siccatives). Anionically stabilised resins containing free 
hydroxyl groups – these include maleinised oils and epoxy esters where the anhydride group is 
opened by adding polyols – can be co-crosslinked. The 
crosslinkers
 
of choice are phenol resins 
(resols), melamine resins and benzoguanamine resins.
Automotive OEM coatings

---

51
Anodic electro deposition primers contain 
coloured pigments
(titanium dioxide, mostly tinted with 
small amounts of carbon black and yellow iron oxide to form grey shades, but red iron oxides are also 
employed), 
extenders
(mainly barium sulphates) and 
corrosion protection pigments
 
(lead or zinc 
chromates, lead silicates). Maleinised oils have excellent wetting properties that are conducive to the 
manufacture of pigment dispersions. The pigment volume concentration for electro deposition prim-
ers, calculated on solids contents, is a relatively low 5 to 10 % by volume. 
Additives
for anodic electro 
deposition primers are levelling agents and anti-settling additives. The primers contained up to 10 % 
co-solvents
, with glycol ethers preferred (e.g. monobutyl ether of ethylene glycol = butyl cellos-
olve, or the monobutyl ether of diethylene glycol = butyl carbitol). The solids content of the anodic 
tank was about 10 to 15 % by weight.
Application process
Anodic electro deposition tanks 
[56, 57]
are operated at a temperature of 25 to 30 °C, a pH value of 
7.5 to 8.5 and a specific conductivity of 5,000 mS/cm. The car body is totally immersed for 2 to 3 
minutes; the deposition current potential is 150 to 250 Volts. The deposition equivalent is 50 to 
Figure 3.4.2: Production of a water-dilutable maleinised oil
Pre-treatment and primers

---

52
70mg/C and the resultant films are 25 to 35 µm thick. After removal from the tank, the coated car 
body is carefully rinsed to remove all soluble materials from the film. The primer is then stoved 
for 20 to 30 minutes at approx. 170 °C. The quantity of coating material removed from the tank 
during deposition is replenished with concentrated coating material.