Automotive Coatings Formulation: Chemistry, Physics und Practices

fungicides
and 
bactericides
selected must 
not adversely affect humans or the environment. Nor must they have a deleterious influence on the 
application behaviour or primer film properties (levelling, yellowing, corrosion resistance). 
Wetting properties
The resins of anionically stabilised electro deposition primers, the maleinised oil and butadiene 
oils, have excellent wetting properties (for pigments and surfaces). Aromatic epoxy resins have 
inferior wetting properties due to their polarity and relatively high glass transition temperatures. 
Pre-treatment and primers

---

56
The epoxy resins are therefore modified. To wet the pigments, a special binder, called a grinding 
resin, is prepared. Wetting of surfaces can also be effected with additives. Wetting agents influ-
ence the surface tension of the primer material. Yet foaming must be avoided. Most additives of 
this kind are surfactants with ionic structures. However, they are not effective in electro deposi-
tion processes due to the difficult deposition behaviour of soluble ions. The focus of attention 
therefore has to be on nonionic compounds. Of course, the wetting properties are influenced by 
the surface itself. The aforementioned pre-treatment materials (see Chapter 3.4.3) have also been 
optimised as regards wetting behaviour.
Adhesion
Good wetting of the surface is a pre-condition for good adhesion. Modified aromatic epoxy resins 
afford excellent adhesion if the surface is prepared well. Various explanations are given for this. 
One is the positive interaction between the aromatic ether structure of the epoxy resins and the 
metals or metal ions (akin to complex bonding). Aliphatic epoxy resins do not have this property. 
The amine groups might also support adhesion. In addition, crosslinking of modified aromatic 
epoxy resins is associated with only a small variation in specific density, compared with other 
crosslinking reactions. That is why the initial physical molecular contacts between resin and 
surface remain stable throughout the film forming process, which is important for adhesion. The 
type of pigments, too, may be beneficial to the adhesion properties. The physical background to 
adhesion is described in more detail in the chapter on primer surfacers (see Chapter 3.5.2).