Automotive Coatings Formulation: Chemistry, Physics und Practices

– 
later 
– 
for PVC copolymers. These 
fatty acids were sourced from peanut oil and castor oil (fatty acids with only one double bond) or 
coconut oil (with saturated fatty acids). A semi-synthetic oil was produced by dehydrogenation of 
castor oil (DCO or dehydrogenated castor oil). The fatty acids thereof consist mainly of 9,11-linoleic 
acid. Like the fatty acids of tung oil, the conjugated double bonds of DCO fatty acids do not take 
up high quantities of oxygen by addition. Instead, film formation by crosslinking takes the form 
of polymerisation reactions (1,4-polymerisation), which is accelerated at
 
elevated temperatures. 
DCO fatty acids were therefore preferred for formulating stoving enamels. Initially, such grades of 
alkyds were combined with amino resins to plasticise them. It was later found that
 
alkyds, mainly 
those which contain sufficient quantities of free hydroxyl groups, can crosslink with amino resins 
(co-crosslinking), and that
 
the resultant films offer an optimum balance of hardness and flexibility 
and are also resistant to solvents and chemicals. With that
 
knowledge, it was only a small step to 
the development of topcoats containing alkyds that were modified with saturated fatty acids that 
contain significant quantities of hydroxyl groups, and contained melamine resins for crosslinking. 
Originally, the sources of those fatty acids were coconut oil. Nowadays, acids from coconut oil are 
used for the production of biodegradable surfactants (e.g. for cosmetic articles), high performance 
lubricants (e.g. for jet engines) and cooling media (e.g. for transformers). Synthetic fatty acids thus 
became more important for alkyds. Synthetic fatty acids are aliphatic, branched monocarboxylic 
acids made from various olefins by the oxo synthesis. Alkyds based on them are distinguished by 
excellent hardness, adequate solubility, yellowing resistance, and weatherability. For pigment-wet-
ting properties and optimum application behaviour (surface wetting, no popping, levelling, and 
flow), it makes sense to combine the synthetic fatty acids with linear fatty acids that bear long 
aliphatic chains and also small quantities of double bonds.