3. MATERIALS AND METHODS
3.1. Materials
Seven binary aggregate mixtures were made out of eight fractions of three quarries. The mixes 
were made in several steps by adding 10% to 20% of volume of fines to coarse material in each 
step for every binary mixture. Table 1 shows the consumables used in the experiments, Figure 2
illustrates the sieving curves for the materials and Table 2 shows the ingredients for the 
mixtures.

---

89
Table 1 – Aggregates used for the experiments
Quarry
Type
Fraction
Riksten
Natural
0 - 4 mm
8 - 16mm
Riksten
Crushed
0 - 2 mm
0 - 4 mm
4 - 8 mm
8 - 16 mm
Ledinge
Cubic crushed
0 - 4 mm
8 - 16 mm
Figure 2 – aggregate sieving curves
Table 2 – Mixtures ingredients
Combo
Fine
Coarse
d
50(fine) 
/ d
50(coarse)
*
Mix1
Riksten Crushed 0-4 mm
Riksten Crushed 8-16 mm
0.12
Mix2
Riksten Crushed 0-2 mm
Riksten Crushed 8-16 mm
0.09
Mix3
Riksten Crushed 4-8 mm
Riksten Crushed 8-16 mm
0.52
Mix4
Riksten Natural 0-4 mm
Riksten Natural 8-16 mm
0.08
Mix5
Ledinge Cubic Crushed 0-4 mm**
Ledinge Cubic Crushed 8-16 mm
0.07
Mix6
Ledinge Cubic Crushed 0-4 mm
Riksten Natural 8-16 mm
0.09
Mix7
Riksten Natural 0-4 mm
Ledinge Cubic Crushed 8-16 mm
0.07
* The ratio of mean diameter of fine aggregate class to mean diameter of coarse aggregate class.
**crushed aggregates formed in a crusher to a cubic shape so they become less angular.