Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-converter slag 
 
Fe: 38.32% 
Cu: 4.03% 
Co: 0.49% 
Ni: 1.97% 
 
Extractant: H
2
SO
4 
(0.2 – 0.35 N)  
Oxygen pressure: 0.45 - 0.59 MPa 
FS: 52 - 270 µm 
L/S: 2.5 – 20 (40 – 5% of solid) 
T: 130°C 
LT: 1 – 4 h 
AS: 840 rpm 
 
 

  Maximum metals dissolution achieved at 4 h of experimental time 

  Increasing of pulp density (especially  from 10 to 40%) led to decreased  metal 
extraction  

  Higher acid concentration improved metals leaching 

  Lower particle size favors metal extraction 

  Increased oxygen pressure improved metals extraction 

 
Conditions of: SL: 10%, 0.35 N acid concentration, T: 130°C, O
2 
pressure 0.59 
MPa,  LT:  4  h,  stirring:  840  rpm  were  found  to  give  optimum  leaching  of:  Cu 
92% (37.1 g/kg) #, Ni >95% (> 18.7 g/kg), Co >95% (> 4.7 g/kg) 
Anand et al. 
(1983)