Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-converter slag 
 
Fe: 38.32% 
Cu: 4.03% 
Co: 0.48% 
Ni: 1.98% 
 
Roasting/leaching 
Roasting agent : (NH
4
)
2
SO
4
 and H
2
SO
4  
Roasting T: 30 – 600°C 
Roasting time: 0.25 – 2 h  
L/S: n.i. 
Extractant: H
2
O 

  Temperature in the range 30-200°C appears to be suitable when H
2
SO
4 
used as 
sulfating agent 

 
Increase  of  temperature  above  200°  leads  to  H
2
SO
4 
evaporation,  hence 
decreases metals extraction 

  Stoichiometric  quantity  of  H
2
SO
4 
is  sufficient  to  reach  satisfactory  metal 
extraction Cu, Co, Ni, Fe 

  Time of 0.5 h appears to give satisfactory extractions of: Cu 90% (36.3 g/kg), 
Ni 95% (18.8 g/kg), Co 100% (4.8 g/kg), Fe 50% (191.6 g/kg) 

  Optimal  conditions:  stoichiometric  requirement  of  H
2
SO
4
,  T:  150°C,  LT:  1  h 
(Co  95%  (4.6  g/kg),  Ni  95%  (18.8  g/kg),  Cu  95%  (38.3  g/kg)  #  and  Fe  70% 
(268.2 g/kg)) 

  Two stage roasting reduces contamination of solution by Fe to 1.5% (5.7 g/kg) 
 
Sukla et al., 
(1986)