Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-flash smelter 
slag 
 
Fe: 46.46% 
Cu: 1.76% 
Co: 0.19% 
Ni: 0.23% 
 
Extractant: FeCl
3
 
FS: <53 – <150 µm 
L/S: 10 
T: 100°C 
LT: <3h – 12 h 
AS: 200 rpm 
 
  

  Excess of ferric iron improves copper extraction from smelter slags 

  Decreasing  of  particle  size  allowed  to  achieve  better  extraction  of  metals, 
especially when FS < 53 µm 

  Increase of leaching time (from 3 up to 6 h) positively affects extraction of Co 
and Ni, whereas none significant changes were observed for Cu 

  Method  applied  for  smelter  slags  allowed  to  achieve  maximum  extraction  of 
54% (9.5 g/kg) # 

 
Conditions  of:  PS  <  53  µm,  LT:  6  h,  T:  100°C,  amount  of  ferric  chloride 
5×stoichiometric were found to give optimum leaching of: Cu 54% (9.5 g/kg) 
#, Ni 77% (1.8 g/kg), Co 44% (0.8 g/kg) 
Anand et al. 
(1980) 

---

CHAPTER 2: COPPER METALLURGICLA SLAGS- CURRENT KNOWLEDGE AND FATE:  
A REVIEW
 
 
42