Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu slag 
 
Fe: 20.7% 
Si: 15.37 
Cu: 1.43% 
Zn: 8.9% 
Co: 0.72% 
 
Extractant: H
2
SO
4 
+ H
2
O
2 
(0 – 125 L/t slag) 
FS: <100 µm 
L/S: 10 
T: 24 – 80°C 
LT: 0.25 – 3 h (15 – 180 min.) 
AS: present (n.i. rpm) 
pH : 2.5 
Eh : 450 – 650 mV 
 
 

 
Increase of the temperature to 60°C significantly improved extraction efficiency 

  High concentration of: Cu, Co, Zn obtained during 60 min. of experiment 

  Silica gel formation (approximately 3-8 g/L) 

  Leaching: Cu 60% (8.6 g/kg), Co 90% (6.5 g/kg), Zn 90% (80.1 g/kg), Fe 90% 
(186.3 g/kg) (2 h, 80°C) 

  Leaching: Cu 80% (11.4 g/kg), Co 90% (6.5 g/kg), Zn 90% (80.1 g/kg), Fe 5% 
(10.4 g/kg) (70°C, pH = 2.5, H
2
O
2 
addition) 

  Optimal dosage of H
2
O
2 
: 62.5 L/ t slag 

  Addition of oxidant significantly decreases Fe content in the solution 

  Leaching at higher redox potential can improve leaching efficiency (time)  e.g. 
Cu: 65% (9.3 g/kg) (450 mV, 180 min) = (650 mV, 60 min)  

  Recovery (selective solvent metal extraction): Cu >99%, Co >96%, Zn >99% 

  Overall  recovery:  Cu  80%  (11.4  g/kg)  #,  Co  90%  (6.5  g/kg),  Zn  90%  (80.1 
g/kg) 
Banza et al. 
(2002) 

---