Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Brass slag 
 
FeO: 1.3% 
(Fe: 1%) 
CuO: 13% 
(Cu: 10.4%) 
ZnO: 69% 
(Zn: 55.4%) 
 
 
Extractant: H
2
SO
4 
(25 g, 30%) 
FS: <100 µm 
L/S: 3 – 8 
T: 10 – 70°C 
LT: 0.083 – 1.33 h (5-80 min) 
AS: 60 – 400 rpm 
 
 
Evaluated parameters: acid concentration, particle size, reaction time, temperature 

  Rotation  speed  does  not  affect  leaching  of  copper  (9%)  (9.2  g/kg),  whereas 
faster  rotation  increases  Zn  leaching  from  60%  (332.4  g/kg)  (50  rpm)  to  93% 
(515.3 g/kg) (150 rpm) 

  Time  necessary  to  reach  Zn  and  Cu  maximum  leaching  were  10  min.  and  30 
min., respectively. Afterwards leaching may decrease 

  Optimum  H
2
SO
4 
concentration  for  Zn  extraction:  25-35%,  H
2
SO
4
  and  for  Cu 
extraction 30-45% H
2
SO
4
. Higher  H
2
SO
4
 concentrations increase the viscosity 
of the solution and inhibit the leaching process 

  Under conditions of 30% H
2
SO
4, 
T 35°C, ~90% (93.5 g/kg) # of Cu is leached 

  Increase  of  LS  ratio  gives  greater  metal  extraction.  L/S  of  5  is  suggested  as 
optimum (Cu 9% (9.2 g/kg), Zn 93% (515.3 g/kg)) 

 
Increasing temperature  favours Cu and Zn leaching:  up to 70°C enhanced  Cu 
leaching, whereas for Zn only up to 35°C 
Ahmed et al. 
(2012) 

---

CHAPTER 2: COPPER METALLURGICLA SLAGS- CURRENT KNOWLEDGE AND FATE:  
A REVIEW
 
 
49