Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-slag 
 
Fe: 36.41% 
Cu: 2.20% 
Zn: 5.92% 
 
Thermal treatment agent: NH
4
Cl 
Extractant: H
2
O 
FS: 75 µm (200 mesh) 
L/S: 2 
T: 280 – 320°C 
LT: 0.33 – 2.33 h (20-140 min) up to 5 h (Fe) 
AS: n.i. 
 
 
Evaluated parameters: temperature, heat treatment time,  

  Increasing reaction time and temperature are favourable to obtain water-soluble 
components 

  Cu, Zn recovery reaches 89.7% (19.7 g/kg) # and 91.5% (54.2 g/kg) during 120 
min. at 320°C, whereas Fe recovery reached approximately 35% (127.4 g/kg) 

  Increasing time of thermal treatment allows to improve Fe recovery (300 min., 
320°C) 

  Two  stage  treatment  is  more  favourable  for  selective  recovery  (heating  120 
min. +  treatment  with NH
4
Cl. 1
st
 step: (approximately 90% of  Cu and  Zn and 
35% Fe recovery), 2
nd
 step: (improved Fe recovery up to 88.3%) 

  Selective  precipitation:  pH  adjusted  to  4,  5.5,  7,  10  aimed  to  precipitate 
compounds  in  the  form  of:  Fe(OH)
3
,  Cu(OH)
2
,  Zn(OH)
2
  and  Ca(OH)
2
/ 
Mg(OH)
2
 

  Reagents recovery: NH
4
Cl recovered by evaporation of solution after selective 
precipitation  stage  and  reused  in  the  process,  ammonia  water  used  for  pH 
adjustment  
Nadirov et al. 
(2013) 
FS: fraction size, L/S: liquid to solid ratio S/L: solid to liquid ratio, T: temperature, LT: leaching time, AS: agitation speed, n.i.: none information provided,  
# presented in Figure 2.5 

---

CHAPTER 2: COPPER METALLURGICLA SLAGS- CURRENT KNOWLEDGE AND FATE:  
A REVIEW
 
 
50