Automotive Coatings Formulation: Chemistry, Physics und Practices

3.4.5.7 Additives
Cathodic electro deposition primers may contain wetting agents, defoamers, and levelling agents. 
It is important to select nonionic materials, as they do not impair tank stability or the deposition 
process. The levelling agents employed are polyacrylates or polyvinyl ethers. The products have 
to be organophilic because they must diffuse into the dispersion particles and be deposited along 
with them so as to be active during film formation. Hydrophilic compounds may be released in 
the dipping tank. Some formulations contain modified siloxanes. Since levelling agents act on the 
surface of the paint layers by floating to the surface during film formation, it is essential to test 
their influence on intercoat adhesion. Naturally, wetting and adhesion of the following paint layer 
(primer surfacers) must not be impaired.
Several patents describe special alkyne diols as defoamers. Co-solvents can also support levelling 
and may act as defoamer. For this reason, some primers in the past contained small amounts of 
Pre-treatment and primers

---

68
glycol ethers. But since emissions of volatile compounds are to be reduced, current formulations 
dispense with co-solvents altogether. As already mentioned, the crosslinking reaction of blocked 
polyisocyanates and modified epoxy resins is catalysed. The preferred catalyst is still dibutyltin 
oxide, which is incorporated into the entire formulation after having been dispersed in resin along 
with pigments. Alternatives are also currently being studied, e.g. bismuth compounds. 
3.4.5.8 Overall primer formulation
A fully formulated cathodic electro deposition primer consists of the main resin dispersion, 
comprising the modified epoxy resin, the crosslinker and the volatile organic acid which acts as 
neutralisation agent, along with the pigment paste containing the special grinding resin, pig-
ments, and the crosslinking catalyst.