Fig. 1.10. Composition of cement paste at different 
stages of hydration.
1.10 
The percentage 
indicated applies only to pastes with enough 
water-filled space to accommodate the 
products at the degree of hydration indicated 
As a more specific example, let us consider 
the hydration of a paste with a water/cement ratio 
of 0.475, sealed in a tube. Let the mass of dry 
cement be 126 g, which corresponds to 40 ml. 
The volume of water is then 0.475 × 126 = 60 
ml. These mix proportions are shown in the lefthand 
diagram of 
Fig. 1.11
, but in reality the cement 
and water are of course intermixed, the water 
forming a capillary system between the unhydrated 
cement particles. 

---

139 
Fig. 1.11. Diagrammatic representation of the 
volumetric proportions of cement paste at different 
stages of hydration 
Let us now consider the situation when the cement 
has hydrated fully. The non-evaporable water 
is 0.23 × 126 = 29.0 ml and the gel water is 
wg 
such that 
whence the volume of gel water is 24.0 ml, and 
the volume of hydrated cement is 85.6 ml. There 
are thus 60 – (29.0 + 24.0) = 7.0 ml of water left 
as capillary water in the paste. In addition, 100 – 

---

140 
(85.6 + 7.0) = 7.4 ml form empty capillaries. If 
the cement paste had access to water during curing 
these capillaries would fill with imbibed water. 
This then is the situation at 100 per cent hydration 
when the gel/space ratio is 0.856, as 
shown in the right-hand diagram of 
Fig. 1.11
. As 
a further illustration, the centre diagram shows 
the volumes of different components when only 
half the cement has hydrated. The gel/space ratio 
is then 
An approach similar to that of Powers, outlined 
above, has been applied to cements containing a 
limestone filler (see p. 
88
).
1.97