Table 1.8. Heat of Hydration of Pure Compounds
1.32 
It may be noted that there is no relation 

---

153 
between the heat of hydration and the cementing 
properties of the individual compounds. Woods, 
Steinour and Starke
1.33 
tested a number of commercial 
cements and, using the method of least 
squares, calculated the contribution of individual 
compounds to the total heat of hydration of cement. 
They obtained equations of the following 
type: heat of hydration of 1 g of cement is 
136(C3S) + 62(C2S) + 200(C3A) + 
30(C4AF) 
where the terms in brackets denote the percentage 
by mass of the individual compounds in cement. 
Later work
1.83 
broadly confirmed the contribution 
of the various compounds to the heat of hydration 
of cement except for C2S whose contribution 
was found to be about one-half of that given 
above. 
Because in the early stages of hydration the 
different compounds hydrate at different rates, 
the 
rate 
of heat evolution, as well as the total 
heat, depends on the compound composition of 
the cement. It follows that by reducing the proportions 
of the compounds that hydrate most rapidly 
(C3A and C3S) the high rate of heat evolution 
in the early life of concrete can be lowered. The 
fineness of the cement also influences the rate of 
heat development, an increase in fineness speeding 
up the reactions of hydration and therefore the 
heat evolved. It is reasonable to assume that the 
early rate of hydration of each compound in cement 
is proportional to the surface area of the cement. 
However, at later stages, the effect of the 
surface area is negligible and the total amount of 
heat evolved is not affected by the fineness of cement. 
The influence of C3A and C3S can be gauged 
from 
Figs 1.15 
and 
1.16
. As mentioned before, 
for many uses of concrete, a controlled heat evolution 
is advantageous and suitable cements have 
been developed. One such cement is low heat 
Portland cement discussed in more detail in 
Chapter 2
. The rate of heat development of this 
and other cements is shown in 
Fig. 1.17
. 

---

154