Table 1.7. Heat of Hydration Developed After 
72 Hours at Different Temperatures
1.30 
Strictly speaking, the heat of hydration, as 
measured, consists of the chemical heat of the reactions 
of hydration and the heat of adsorption 
of water on the surface of the gel formed by the 
processes of hydration. The latter heat accounts 
for about a quarter of the total heat of hydration. 
Thus, the heat of hydration is really a composite 
quantity.
1.24 
For practical purposes, it is not necessarily the 
total heat of hydration that matters but the rate of 
heat evolution. The same total heat produced over 
a longer period can be dissipated to a greater degree 
with a consequent smaller rise in temperature. 
The rate of heat development can be easily 
measured in an adiabatic calorimeter, and typical 
time–temperature curves obtained under adiabatic 
conditions are shown in 
Fig. 1.14
. (The ratio 
1:2:4 represents the proportion by mass of cement: 
fine aggregate:coarse aggregate.) 

---

152 
Fig. 1.14. Temperature rise in 1:2:4 concrete 
(water/cement ratio of 0.60) made with different 
cements and cured adiabatically.
1.31 
The 
total heat of hydration of each cement at three 
days is shown (Crown copyright) 
For the usual range of Portland cements, 
Bogue
1.2 
observed that about one-half of the total 
heat is evolved between 1 and 3 days, about 
three-quarters in 7 days, and 83 to 91 per cent of 
the total heat in 6 months. The actual value of the 
heat of hydration depends on the chemical composition 
of the cement, and is very nearly a sum 
of the heats of hydration of the individual compounds 
when hydrated separately. It follows that, 
given the compound composition of a cement, its 
heat of hydration can be calculated with a fair degree 
of accuracy. Typical values of the heat of hydration 
of pure compounds are given in 
Table 1.8
.