Table 1.9. Compound Composition Limits for 
Cements of ASTM C 150-09 
The difference in the early rates of hydration 
of C3S and C2S – the two silicates primarily responsible 
for the strength of hydrated cement 
paste – has been mentioned earlier. A convenient 
approximate rule assumes that C3S contributes 
most to the strength development during the first 
four weeks and C2S influences the gain in 
strength from 4 weeks onwards.
1.35 
At the age 
of about one year, the two compounds, mass for 
mass, contribute approximately equally to the ultimate 
strength.
1.36 
Pure C3S and C2S have been 
found to have a strength of about 70 MPa (10 000 
psi) at the age of 18 months, but at the age of 7 
days C2S had no strength while the strength of 
C3S was about 40 MPa (6000 psi). The usually 
accepted development of strength of pure compounds 
is shown in 
Fig. 1.18
. 

---

157 
Fig. 1.18. Development of strength of pure 
compounds according to Bogue
1.2 
However, these relative values of the contribution 
to strength of the individual compounds in 
Portland cement have been challenged.
1.87 
Tests, 
using particles with the same size distribution and 
at a fixed water/solid ratio of 0.45, have shown 
that, up to at least the age of 1 year, C2S exhibits a 
lower strength than C3S. Nevertheless, both silicates 
are much stronger than C3A and C4AF, although 
the latter compound exhibits a significant 
strength while C3A has a negligible strength
1.87 
(see 
Fig. 1.19
). 

---

158 
Fig. 1.19. Development of strength of pure