Fig. 1.15. Influence of C3A content on heat 
evolution
1.32 
(C3S content approximately constant) 
Fig. 1.16. Influence of C3S content on heat 
evolution
1.32 
(C3A content approximately constant) 

---

155 
Fig. 1.17. Development of heat of hydration of 
different cements cured at 21 °C (70 °F) (water/ 
cement ratio of 0.40)
1.34 
The quantity of cement in the mix also affects 
the total heat development: thus the richness of 
the mix, that is, the cement content, can be varied 
in order to help the control of heat development. 
Influence of the compound composition 
on properties of cement 
In the preceding section, it was shown that the 
heat of hydration of cement is a simple additive 
function of the compound composition of cement. 
It would seem, therefore, that the various 
hydrates retain their identity in the cement gel, 
which can be considered thus to be a fine physical 
mixture or to consist of copolymers of the hydrates. 
A further corroboration of this supposition 
is obtained from the measurement of specific surface 
of hydrated cements containing different 
amounts of C3S and C2S: the results agree with 
the specific surface areas of hydrated neat C3S 
and C2S. Likewise, the water of hydration agrees 

---

156 
with the additivity of the individual compounds. 
This argument does not, however, extend to all 
properties of hardened cement paste, notably to 
shrinkage, creep, and strength; nevertheless, the 
compound composition gives some indication of 
the properties to be expected. In particular, the 
composition controls the rate of evolution of the 
heat of hydration and the resistance of cement to 
sulfate attack, so that limiting values of oxide or 
compound composition of different types of cement 
are prescribed by some specifications. The 
limitations of ASTM C 150-09 are less restrictive 
than they used to be (see 
Table 1.9
).