Evaluation Of Thermophysical Properties, Friction Factor And Heat Transfer Of Alumina Nanofluid Flow In Tubes

Figure 2.4. Hysteresis observed on viscosity for alumina (47 nm, 7%)- water nanofluid, Mintsa et al. 
(2007). 
 
Lee  et  al. (2008) measured the  effective viscosities and thermal  conductivity of Al
2
O
3
-
water  nanofluid  for  low  volume  concentration  of  nanoparticles  ranging  from  0.01%  to 
0.3%. They used ultrasonic vibration for 5 hours to finely disperse the particle into the 
solution. They used the oscillation type viscometer to measure the viscosity of nanofluid 
for a temperature range of 21 to 39°C. They tested their experimental setup with DI water 
with a measurement uncertainty of ±1.8%. A maximum increment in viscosity by 2.9% at 
concentration  of  0.3%  compared  to  the  base  fluid  is  reported.  They  found  a  nonlinear 
relationship between the viscosity and temperature (see Figure 2.5) even at low volume 
concentration (0.01%−0.3%). This was found to contradict the Einstein model that serves 
to  be  valid  for  particle  concentration  less  than  2  %  vol.  which  predicts  a  linear 
relationship between the viscosity and temperature. 
 

---

29 
 
 
Figure 2.5. Nanofluid Viscosity vs. Temperature for low volume fraction of nanoparticles