Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

with crystalline slag (CS), granulated slag (GS) and  
control growth without slag supplementation.  
OD 600 nm: optical density of solution at a wavelength of 600 nm. 
 
6.3.2  pH evolution 
In abiotic UPW experiments, the pH was gradually increasing up from 5.6 to 6.7 (CS) and 7.6 
(GS)  during  42  days  of  incubation  and  then  was  kept  on  relatively  stable  level  until  the 
experiment (Figure 6.2 A). Oscillations of pH in the GM experiments were negligible due to 
the  GM  buffering  capacity  and  was  7.8  (±0.1).  The  pH  in  the  biotic  experiment  with  CS 
increased during 14 days (from 7.8 to 9.2) and was then decreasing gradually to 8.1 (56 days). 
The pH value in the biotic experiment carried out with GS increased from 7.8 up to 9.2 during 
14 days and was maintained on a stable level over the entire experiment duration. 
 

---

CHAPTER 6: BACTERIALLY MEDIATED WEATHERING OF CRYSTALLINE AND AMORPHOUS Cu-SLAGS
 
173