Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

 
FIGURE 6.2 Evolution of pH in the experiments carried out with  
crystalline - CS (A) and granulated - GS (B) slag.  
(GMB: growth medium with bacteria, GM: growth medium, UPW: ultrapure water) 
 
 
6.3.3  Elements release under abiotic and biotic conditions 
Release of the major and minor elements resulting from experiments is presented in  Figures 
6.3 and 6.4 as the cumulative curves expressed in mg of elements released per kg of slag.  
The  influence  of  GM  on  Si  release  increased  gradually  throughout  the  experiment,  while  a 
lower release was observed in UPW. A cumulative release of Si in biotic solution presented a 
steeper  trend  compared  to  GM.  After  112  days  of  CS  incubation,  the  amount  of  Si  released 
was  434.4  and  509.2  mg/kg  for  biotic  experiments  (GMB  total  and  GMB  <0.22  µm, 
respectively)  and  345.9  mg/kg,  179.9  mg/kg  for  abiotic  experiments  (GM  and  UPW, 
respectively).  Likewise,  for  GS  the  cumulative  curves  showed  a  gradual  increase  of  the  Si 
content in the solutions and reached 141.8 mg/kg, 304.5 mg/kg, 501.0 and 617.5 mg/kg at the 
end  of  the  experiment  for  UPW,  GM,  GMB  <0.22  µm  and  GMB  total,  respectively. 
Mobilization of Fe in abiotic experiments (UPW and GM) was limited and reached 2.1 mg/kg 
(UPW)  and  10.1  mg/kg  (GM)  after  112  days  of  experiment  with  CS.  A  slightly  higher 
quantity of Fe in GM (21.9 mg/kg) was observed compared to its content in UPW (2.8 mg/kg) 
after  112  days  of  experiment  with  GS.  A  considerable  increase  of  Fe  was  observed  in  the 
biotic solution to which 237.2 mg/kg (GMB <0.22 µm), 292.6 mg/kg (GMB total) and 382.8 
mg/kg (GMB <0.22 µm), 432 mg/kg (GMB total) was released after 112 days for CS and GS, 
respectively.  
 

---