Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

iv) For granulometry  
The  granulometry  (4  mm  <  f  <  0.06  mm)  was  determined  only  for  granulated  slags.  The 
material was sieved to separate different
 
grain sizes and fractions were weighed to determine 
the relative distribution of particular fractions per kilogram of granulated slag. 
 
3.1.2.2  Leaching solutions preparation 
i) Solutions for organic acid leaching 
Leaching  experiments  were  performed  using  humic  (HA)  and  fulvic  acids  (FA)  as  well  as 
artificial root exudates (ARE). The HA and FA solutions were prepared by dissolving 20 mg 
of  commercial  (Suwannee  River,  International  Humic  Substances  Society)  humic  (HA)  or 
fulvic acid (FA) in 1 L of MilliQ water (20 mg/L) and were pre-set at initial pH of 4.4. The 
ARE solution corresponded to the rhizosphere composition described by Baudoin et al. (2003) 
and  contained:  glucose  (3.31  g/L),  fructose  (3.31  g/L),  sucrose  (3.15  g/L),  citric  acid  (1.77 
g/L), lactic acid (1.66 g/L), succinic acid (1.63 g/L), alanine (0.74 g/L), serine (0.97 g/L) and 
glutamic  acid  (0.81  g/L).  The  initial  pH  of  ARE  solution  was  2.9  and  4.4  for  two  different 
treatments.  The  pH  value  of  the  solutions  was  adjusted  using  HNO
3 
or  NaOH.  The  ARE 
solution  is  composed  of  simple,  low  molecular  weight  organic  acids,  whereas  HA/FA  are 
characterized  by  a  more  complex  structure  and  higher  molecular  weight  (Schulten  & 
Schnitzer, 1993).