O‘zmu xabarlari Вестник нууз acta nuuz

 
 
 
 
 
Figure 5. 
Variation of the average porosity of nanostructured aluminum oxide films anodized in oxalic acid as a function of the 
concentration and temperature of the electrolyte and the voltage 
For samples synthesized at 25 °C in the presence of 0.3 M oxalic acid electrolyte during the anodizing process, a decrease 
in the average porosity was observed with increasing anode voltage, and a small change in porosity was observed at 5 and 15 ºC. 
In the anodization process, the reverse of the above results was observed when the electrolyte concentration was 1 M, ie the 
average porosity increased significantly with increasing anode voltage at electrolyte temperatures of 10 and 15 ºC. 
Conclusions. 
In this work, anodic aluminum oxide nanostructured coatings were synthesized and characterized from a 
commercial aluminum alloy by varying the oxalic acid concentration, temperature, and anodization voltage. 
The obtained AAO films presented short-range pore arrangements that changed with the concentration, temperature and 
synthesis voltage; pore diameters and interpore distances which varied only with anodizing voltage; thicknesses that changed 
significantly with concentration, temperature and voltage, and porosities that varied predominantly with voltage and electrolyte 
temperature. The key role of voltage on pore dimension when oxalic acid is used as electrolyte has been demonstrated. 
 
REFERENCES
1.
Jagminas A., Vrublevsky I. Anodizing of aluminum under the burning conditions // Nanostructured anodic metal oxides, 
2020. P. 89–122. doi:10.1016/b978-0-12-816706-9.00003-0. 
2.
Fernández-Romero L., Montero-Moreno J.M., Pellicer E., Peiró F., Cornet A., Morante J.R., Müller C. Assessment of the 
thermal stability of anodic alumina membranes at high temperatures // Materials chemistry and physics, 2008. №111(2-3). 
P. 542–547. doi:10.1016/j.matchemphys.2008.05. 
3.
Crouse D., Lo Y.H., Miller A.E., Crouse M. Self-ordered pore structure of anodized aluminum on silicon and pattern 
transfer // Applied physics letters, 2000. №76(1). P. 49–51. doi:10.1063/1.125652. 
4.
Tomassi P., Buczko Z. Aluminum anodic oxide AAO as a template for formation of metal nanostructures // Electroplating 
of nanostructures, 2015. doi:10.5772/61263 
5.
Jai Poinern G.E., Ali N., Fawcett D. Progress in nano-engineered anodic aluminum oxide membrane development // 
Materials. 2011. № 4(3). P. 487-526. 

---