O‘zmu xabarlari Вестник нууз acta nuuz

Намуна 
𝒅𝒑
̅̅̅̅
 
(нм)
 
𝒅𝒊
̅̅̅
 (нм) 
𝒆̅
 (μм) 
𝐏
̅
 (%) 
С0.3 Т5 В20 
41.1±3.3 
49.9±4.3 
3.7±0.6 
28.2±1.8 
С0.3 Т5 В30 
47.9±3.4 
60.8±4.3 
6.2±0.5 
26.1±1.6 
С0.3 Т5 В40 
54.1±3.2 
76.1±6.3 
9.4±0.5 
28.9±4.2 
С0.3 Т15В20 
41.5±3.2 
49.9±4.3 
5.8±0.8 
25.2±0.8 
С0.3 Т15В30 
47.4±3.3 
62.4±6.7 
10.1±1.0 
22.2±2.5 
С0.3 Т15В40 
54.6±3.1 
72.1±4.6 
20.3±0.5 
26.3±0.7 
С0.3 Т25В20 
41.3±2.7 
51.2±4.3 
8.9±0.7 
33.2±0.6 
С0.3 Т25В30 
46.7±2.7 
62.7±7.4 
19.7±1.1 
32.1±0.3 
С0.3 Т25В40 
50.8±2.8 
70.6±4.8 
31.6±0.8 
26.8±0.4 
С1 Т5 В10 
26.8±2.5 
36.5±3.6 
5.7±0.3 
13.2±0.5 
С1 Т5 В12 
30.7±2.8 
40.8±4.4 
9.5±0.2 
20.2±0.9 
С1 Т5 В15 
31.3±2.3 
44.9±5.2 
16.8±0.5 
19.1±2.8 
С1 Т10 В10 
28.1±3.2 
38.2±5.1 
9.9±0.2 
15.4±1.7 
С1 Т10 В12 
30.8±2.3 
40.1±3.9 
14.8±0.2 
26.6±0.7 
С1 Т10 В15 
33.4±3.4 
45.5±4.4 
21.4±0.6 
27.8±0.3 
С1 Т15 В10 
28.0±2.3 
38.1±4.2 
18.9±0.4 
19.7±0.5 
С1 Т15 В12 
28.3±3.1 
42.5±4.7 
25.9±0.3 
20.8±0.6 
С1 Т15 В15 
33.8±2.5 
47.3±4.6 
57.9±0.6 
24.9±2.8 

---

O‘zMU xabarlari Вестник НУУз ACTA NUUz
 
KIMYO 
3/1 2022 
- 342 -
Fig. 1 present the SEM images of the nanostructured oxide coatings obtained by anodic oxidation in 0.3 and 1 M oxalic 
acid solution, respectively, at different temperatures and voltages. In each case, the respective SEMs are presented below the 
micrographs. 
 
 
 
 
 
 
 
 
 
 
 
Figure 1
. Two-steps anodized porous AAO membrane SEM results. 
Scale: a) 100 and b) 30 nm 
After two-steps anodizing, the pores in the porous AAO membrane were sorted, porous membranes with enlarged 
dimensions and a flat surface were obtained. 
Pore Diameter 
The diameter of the pores of the AAO membrane formed as a result of anodic oxidation of aluminum plastic was 
determined as a function of the parameters of the anodizing process: anode voltage, electrolyte concentration and temperature 
(Fig. 2). The results of anodic oxidation of aluminum in the presence of 0.3 and 1 M oxalic acid electrolytes showed that during 
the anodizing process the electrolyte temperature had almost no effect on the formation of the diameter of the pores of the AAO 
membrane. 
 
 
 
 
 
Figure 2. 
Variation of the average pore diameter of nanostructured aluminum oxide films anodized in oxalic acid as a function of 
the concentration and temperature of the electrolyte and the voltage 
During the anodizing process, it was observed that as the voltage increased from 10V to 40V, the diameter of the pores 
also increased linearly, while the diameter of the pores decreased as the electrolyte concentration changed from 0.3M to 1M. 
Interpore Distance 
In the porous AAO membrane formed as a result of anodic oxidation of aluminum, the interaction between the 
parameters of the anodizing process: the anode voltage, electrolyte concentration and temperature dependence of the size of the 
porosity distance was studied (Fig. 3). In this process, similar results were observed for the above porosity diameter properties, 
i.e., it was found that the electrolyte temperature had almost no effect on the measurement of the distance between the pores.