Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

 
FIGURE 8.1 Life-cycle of metallurgical slag including the ultimate stages to be undertaken  
prior implementing the final management strategy. 

---

CHAPTER 8: GENERAL DISCUSSION AND PERSPECTIVES
 
 
234 
 
8.2
 
Research overview and relevance 
This  PhD  work  aimed  at  evaluating  the  environmental  stability  of  slags  issued  by  copper 
smelting  activities.  Cu-slags  resulting  from  different  periods  of  industrial  activities  and 
various  pyrometallurgical  processes  were  chosen  for  comparative  studies  (Figure  8.2). 
Experimental part of this work assembles the results concerning characterization of four types 
of Cu slags (historical slag, shaft furnace slag, granulated slag and lead slag) and comparison 
of  their:  i)  chemical  and  mineral  phase  compositions  (Chapter  4)  ii)  leaching  susceptibility 
under  exposure  to  different  pH-stat  conditions  (Chapter  4),  iii)  weathering  enhancement  by 
organic acids  commonly found  in  soil environment  and (Chapter 5) iv) bacterially mediated 
weathering  (Chapter  6).  In  these  studies  related  to  environmental  aspects  (Chapters  4-6) 
special  attention  was  given  to  the  release  of  metallic  contaminants  such  as  Cu,  Zn  and  Pb. 
Another important  point of this  work was to  consider the future  application of studied slags 
for  metal  recovery  by  implementing  biological  extraction  method  (Chapter  7).  Different 
scenarios  evaluated  in  this  work  aimed  at  fulfilling  the  research  objectives  specified  in 
Chapter  1.  An  overview  of  the  results  obtained  and  conclusions  drawn  are  presented  and 
discussed. The outlook of the perspectives arising from this work as well as aspects related to 
contaminated sites are presented.