Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

7.3.3.2  Slags alteration under exposure to P. fluorescens 
Alteration features observed on slag grains from the incubations with P. fluorescens were less 
pronounced  (Figure  7.8)  compared  to  those  resulting  from  the  incubations  with  A. 
thiooxidans. The CS grains resulting from  abiotic experiments were barely altered as shown 
in  Figure  7.8  A.  The  breakdown  of  sulfides  was  commonly  found  (Figure  7.8  B),  whereas 
round-shaped  alteration  zones  on  fayalite  were  observed  occasionally  (Figure  7.8  C). 
Likewise, AS was less altered with P. fluorescens as compared to acidic experiments with A. 
thiooxidans (Figure 7.7). Removal of Cu-droplets from glass was found frequently (Figure 7.8 

---

CHAPTER 7: COMPARISON OF Cu, Zn AND Fe BIOLEACHING FROM Cu-METALLURGICAL SLAGS IN THE 
PRESENCE OF PSEUDOMONAS FLUORESCENS AND ACIDITHIOBACILLUS THIOOXIDANS
 
 
219 
 
D), only with a lower degree of liberation as compared to AS exposed to acidic leaching by A. 
thiooxidans (Figures 7.7 and 7.8).