Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Amorphous slag  
Amorphous slags  exposed to abiotic solutions were found to be strongly  perforated (Figures 
7.7  A1  and A2). An important  removal  of Cu-droplets  from  glass was  noted (Figure 7  A2). 
Dissolution features  of grains  resulting from  biotic incubation at  3 % pulp density exhibited 
similar  features  to  those  resulting  from  abiotic  incubations  (Figures  7  B1  and  B2),  whereas 
grains  resulting  from  the  biotic  incubation  at  1  %  pulp  density  displayed  strong  alteration 
(Figure  7.7  C1  and  C2).  The  changes  on  AS  (PS:  1-2,  PD:  1  %)  were  visible  even  at 
macroscale  (Figure  S2  Supplementary  materials).  The  color  with  biotic  treatment  changed 
from  brownish  to  white  and the material  became friable.  In  contrast,  the  original material  is 
vitreous and angular (Potysz et al., 2016b). According to SEM observations, nearly complete 
removal  of  metallic  contaminants  was  achieved  because  only  the  remaining  impurities 
entrapped within the newly formed crystals could be ascertained (Figure  7.7 C1). Long-term 
(40 days) exposure of AS to a strongly biological acidic solution resulted in the conversion of 
the  material  to  calcium  sulfate  with  impurities  of  Si,  Cu,  Pb  and  Fe  according  to  energy 
dispersive spectroscopy (EDS). 

---

CHAPTER 7: COMPARISON OF Cu, Zn AND Fe BIOLEACHING FROM Cu-METALLURGICAL SLAGS IN THE 
PRESENCE OF PSEUDOMONAS FLUORESCENS AND ACIDITHIOBACILLUS THIOOXIDANS
 
 
217