7.3.2.2   Contribution of P. fluorescens to metal solubilization 
During the initial stages  of the bioleaching experiments, the values of extracted metals were 
generally  low  (Figure  7.4).  During  the  initial  stages  of  the  experiments  (3  days),  P. 
fluorescens  improved  metal  extraction  from  CS  by  factors  up  to  3.4  (Cu),  1.2  (Zn)  and  1.3 
(Fe) (Figure 7.4) compared to experiments performed in the presence of growth media alone. 
Likewise, leaching under biotic conditions with AS was improved by factors of 1.6 (Cu) and 
4.0 (Fe) compared to  abiotic leaching, whereas  Zn release was  initially higher under  abiotic 
conditions  (Figure  7.5).  Significant  differences  between  biotic  and  abiotic  experiments 
occurred after 30 days when the amount of metals leached out under biotic conditions was up 
to 26.7 times (Fe) and 60.0 times (Fe) higher as compared to abiotic leaching for CS and GS, 
respectively. After 40 days of incubation, the amount of metals released was 585 mg/kg (Cu), 
166  mg/kg  (Zn)  and  936  mg/kg  (Fe)  for  the  biotic  incubation  with  CS  (Figure  7.4).  At  the 
same  time,  the  amount  of  metals  leached  out  in  the  biotic  incubation  with  AS  reached  474 
mg/kg (Cu), 200 mg/kg (Zn) and 790 mg/kg (Fe) (Figure 7.5). The values of extracted metals 
under abiotic conditions did not exceed 177 mg/kg (Cu), 3 mg/kg (Zn), 8 mg/kg (Fe) for CS 
(Figure 7.4) and 99 mg/kg (Cu), 2 mg/kg (Zn), 15 mg/kg (Fe) for AS (Figure 7.5). 
 

---

CHAPTER 7: COMPARISON OF Cu, Zn AND Fe BIOLEACHING FROM Cu-METALLURGICAL SLAGS IN THE 
PRESENCE OF PSEUDOMONAS FLUORESCENS AND ACIDITHIOBACILLUS THIOOXIDANS
 
 