Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

7.3.1.2   P. fluorescens pH profiles 
The pH profiles in  abiotic and biotic batch experiments with  P. fluorescens are displayed in 
Figure 7.1 E and F. The pH in the abiotic batches was stable due to the buffering capacity of 
the solution  (i.e., addition of 6 g/L of Tris). However, despite the presence of Tris  buffer in 
biotic  medium,  a  pH  increase  was  observed  (Yin  et  al.,  2014).  The  pH  profiles  from  biotic 
experiments  were  comparable  for  both  slag  types  tested.  At  the  early  stage  of  the  biotic 
experiments performed with particle sizes 1-2 mm, the pH increased to 8.0 (PD 1 %) and 8.8 
(PD  3  %)  in  the  case  of  CS  and  7.8  (PD  1  %)  and  8.3  (PD  3  %)  for  AS.  At  the  end  of  the 
experiments (40 days), the values increased up to 9.5-9.7 and 9.8 for CS and AS, respectively. 
An  increase  in  the  pH  values  during  batch  incubations  with  finer  particles  was  less 
pronounced and after 40 days of batch incubations, the pH values were 7.3-7.4 and 7.5-7.6 for 
CS and AS, respectively (Figure 7.1 E and F). 

---

CHAPTER 7: COMPARISON OF Cu, Zn AND Fe BIOLEACHING FROM Cu-METALLURGICAL SLAGS IN THE 
PRESENCE OF PSEUDOMONAS FLUORESCENS AND ACIDITHIOBACILLUS THIOOXIDANS
 
 
209 
 
 
 
FIGURE 7.1 Evolution of pH throughout the experiment with A. thiooxidans (A-D) and