Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Intermetallic phases accommodating metals and their admixtures, which do not correspond 
to  any  known  minerals  were  identified  only  in  the  GS  and  LS.  Copper  droplets  commonly 
occur in the amorphous glass of the GS. Due to the small size of these droplets, their electron 
microprobe analysis could not be performed. For this reason, quantitative analyses of copper 
droplets were performed using SEM-EDS (Table 4.5). Analysis of droplets distributed within 
the glass shows that Cu has
 
a
 
content ranging
 
from 86.7 up to 92.6%, but
 
some other metals
 
also  occur  as  impurities.  Droplets  contain  relatively  high  concentrations  of  Pb  and  As  that 
reach even up to 6.0-7.0 wt.% (Table 4.5). The intermetallic phase identified in  LS contains 
up  to  91.4  wt.%  of  Pb  and  4.52  %  of  Fe  (Table  4.5).  Although,  its  occurrence  was  rarely 
observed  and  the  number  of  analyses  was  limited,  it  appears  to  be  the  most  important  Pb-
carrier responsible for a high bulk Pb content in this material.  

---

CHAPTER 4: CHARACTERIZATION AND pH-DEPENDENT LEACHING BEHAVIOUR OF HISTORICAL AND MODERN COPPER SLAGS
 
 
116 
 
TABLE 4.5 Sulfides and intermetallic phases identified in the studied slags.  
Chemical 
compounds  
wt.%