Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

FIGURE 4.2 X-RAY powder diffraction patterns of copper slags.  
(Mineral names abbreviations after Whitney and Evans (2010): 
Fa: fayalite, Di: diopside, Sp: sphalerite) 
 

---

CHAPTER 4: CHARACTERIZATION AND pH-DEPENDENT LEACHING BEHAVIOUR OF HISTORICAL AND 
MODERN COPPER SLAGS
 
 
110 
 
 
FIGURE 4.3 Scanning electron microscope images of the phases identified in the copper slags.  
Presenting:  A1  and  A2-  Historical  slags  (A1-  Fayalite  embedded  in  silicate  glass  and  commonly 
occurring  sulfides,  A2-  pyrrhotite  and  bornite  growing  between  the  crystal  of  fayalite),  B1  and  B2-
Shaft  furnace  slag  (B1-  Pyroxene:  diopside  crystals  surrounded  by  glassy  matrix,  B2-  bornite 
embedded between diopside crystals) C1 and C2- Granulated slag (C1- amorphous glass with widely 
dispersed  copper  droplets  and  occasionally  identified  crystals  of  hercynite,  C2-  copper  droplets 
reaching  the  size  of  17  µm),  D1  and  D2-  Lead  slag  (D1-  Elongated  fayalite  crystals  present  within 
glassy  matrix  and  sulfides:  sphalerite  occurring  as  volumetrically  major  phase  and  bornite,  D2- 
Bornite occurring between elongated fayalite crystals). 

---

CHAPTER 4: CHARACTERIZATION AND pH-DEPENDENT LEACHING BEHAVIOUR OF HISTORICAL AND 
MODERN COPPER SLAGS
 
 
111