Asian Journal of Multidimensional Research (ajmr)

 

Figure 1. Special ironing board (a), steam electric (b), electric (c) irons. 

Steam-electric  irons  are  a  combination  of  steam  iron  and  electric  iron,  in  which  dry  steam  is 

formed  by  simple  heating.  Steam  -  water  is  supplied  through  a  flexible  hose  mounted  on  the 

---

ISSN: 2278-4853         Vol 10, Issue 9, September, 2021        Impact Factor: SJIF 2021 = 7.699 

Asian Journal of Multidimensional Research (AJMR)

 

https://www.tarj.in

 

308 

 

AJMR 

electric iron  (Fig. 1, b and c) and the water is  heated to steam. The heating temperature of the 

iron is 60-2300 C, the weight of the iron is 2.1 kg. 

 

Figure 2. TVGPTA 120 P pneumatic press (v) 

The  presses  allow  to  mechanize  the  most  labor-intensive  operations  in  wet-heating,  increase 

productivity, improve the quality  of processing  and facilitate the work of workers. The presses 

differ  in  the  type  of  drive,  the  pressing  force  and  the  type  of  pads.  The  presses  can  be 

mechanical, electrical, pneumatic or hydraulic (Figure 2). 

Evaporation. Evaporation is the process of wetting and heating the fabric under the influence of 

steam pressure, not under the influence of heated surfaces. Evaporation reduces the tension in the 

fabric  fibers,  which  makes  the  fibers  non-shiny.  Fabrics  are  steam-decocted  before  use  in 

garment factories. When it evaporates, wet steam is sprayed on the fabric. Wet steam moistens 

and heats the fabric. The fibers swell and heat from moisture. The kinetic energy of gas particles 

has a mechanical effect on the fibers. 

The wet-heat treatment of the fabric is used to shape the details of the garment and to finish the 

product. During wet-heating, the fabric is moistened, exposed to heat and pressure using an iron 

and press. 

As a result of pressure on the fabric, the detail is given the desired shape, the edges are bent, the 

fabric is formed, wrinkles and uneven areas in the fabric are corrected. 

Moisture is removed and the fabric is cooled to maintain the shape given to the detail. 

Wet-heat treatment has a significant impact on product quality and product appearance. 

The wet-heat treatment process is divided into 3 stages: 

1. Preparation of the fabric for molding. 

2. Shaping the fabric. 

3. Reinforce the given form. 

The temperature of the work equipment in stage 2 should be 105-12000 C. The shape formed in 

step 3 should be retained when the fabric fiber cools rapidly. It is known from scientific research 

that the heat retention of a fiber does not change at the following temperatures: 

---

ISSN: 2278-4853         Vol 10, Issue 9, September, 2021        Impact Factor: SJIF 2021 = 7.699