A review of Functional Separators for Lithium Metal Battery Applications

Figure 18. 
(
a
)
 
Ex-situ GPE and in situ GPE. (
b
) Gelation via cross-linking of polymers. Reprinted with 
permission from [164]. Copyright (2018) John Wiley and Sons. 
With the same aim of enhancing mechanical properties and ionic conductivity simultaneously, 
Yang and co-workers synthesized composite electrolytes. They prepared a 3D interconnected porous 
structure and increased the affinity with liquid electrolytes via compositing bacterial cellulose (BC) 
and Li
0.33
La
0.557
TiO
3
nanowires (LLTO NWs) into the aerogel matrix [165] (Figure 19). The affinity 
provided excellent wettability, and a composite gel electrolyte (CGE) exhibited a Young’s modulus 
of 1.15 GPa. Furthermore, it exhibited a high ion transference number of 0.88. The robust BC skeleton 
and LLTO NWs resulted in the suppression of dendritic growth by inducing stable ion deposition. 
Figure 18.
(
a
) Ex-situ GPE and in situ GPE. (
b
) Gelation via cross-linking of polymers. Reprinted with
permission from [
164
]. Copyright (2018) John Wiley and Sons.
With the same aim of enhancing mechanical properties and ionic conductivity simultaneously,
Yang and co-workers synthesized composite electrolytes. They prepared a 3D interconnected porous
structure and increased the a
ffi
nity with liquid electrolytes via compositing bacterial cellulose (BC)
and Li
0.33
La
0.557
TiO
3
nanowires (LLTO NWs) into the aerogel matrix [
165
] (Figure
19
). The a
ffi
nity
provided excellent wettability, and a composite gel electrolyte (CGE) exhibited a Young’s modulus of
1.15 GPa. Furthermore, it exhibited a high ion transference number of 0.88. The robust BC skeleton
and LLTO NWs resulted in the suppression of dendritic growth by inducing stable ion deposition.
Materials