Ўзбекистон республикаси фанлар академияси навоий бўлими ташкил этилганининг 5 йиллигига бағишланган “фан, таълим ва ишлаб чиқаришнинг

Фойдаланган адабиётлар 
1.
Борисов О.М., Глух А.К. Кольцевые структуры и линеаменты Средней Азии. -
Т.: Фан, 1982. - 123с.
2. Нурходжаев А.К., Тогаев И.С., Шамсиев Р.З. Методическое руководство по 
составлению космогеологической карты Республики Узбекистан на основе цифровых 
космоснимков. - Т.: ГП «ИМР», 2017. - 200с. 

---

МЕЖДУНАРОДНАЯ НАУЧНО-ПРАКТИЧЕСКАЯ КОНФЕРЕНЦИЯ 
«ИНТЕГРАЦИЯ НАУКИ, ОБРАЗОВАНИЯ И ПРОИЗВОДСТВА – ЗАЛОГ ПРОГРЕССА И 
ПРОЦВЕТАНИЯ», ТОМ I, ГОРОД НАВОИ, РЕСПУБЛИКА УЗБЕКИСТАН, 2022 
- 298 - 
UDC 669.127.44 
INVESTIGATION OF SEPARATION OF IRON 
FROM COPPER SLAG BY RECOVERY 
Tolibov B.I., Axmedov M.S., Murtozayeva M.M. 
Navoi state university of mining and technologies, 
[e-mail]
 
 
This paper examines the separation of iron alloys from magnetic compounds 
obtained by magnetic separation to the metallic state by adding additives. 
В данной работе рассматривается отделение сплавов железа от 
магнитных соединений, полученных методом магнитной сепарации, до 
металлического состояния путем добавления добавок. 
 
Key words: slag, grinding, magnetic separator, recoveries, magnetic and 
non-magnetic fraction. 
Ключевые слова: шлак, измельчение, магнитный сепаратор, 
извлечение, магнитная и немагнитная фракция. 
Two different products were obtained by magnetic separation (magnetic and 
non-magnetic fraction). The magnetic fraction composition is mainly FeO, Fe
3
O
4
, 
Fe
2
O
3
and Fe
2
SiO
4
. Calcium oxide (CaO) and mixed additives were added during 
the conversion process as they help to restore the mineral phase of copper slag [1-
3]. 
It was found that calcium oxide combines well with SiO2 to form CaSiO
3
and can quickly replace FeO in the fayalite, resulting in increased activity of free 
FeO in the slag. 
CaO + 2FeO · SiO
2
→ CaO · SiO
2
+ 2FeO (1) 
FeO + Fe
2
O
3
→ Fe
3
O
4
(2) 
After the above reaction, FeO (hematite, magnetite and viscite) are formed. 
The FeOs react with C and return to the Fe state. Recovery of iron from oxides is 
carried out by a gradual transition from high oxides to low oxides according to 
the following scheme [4-5]. 
Fe
2
O
3
→ Fe
3
O
4
→ FeO → Fe 
According to the Fe-O diagram, not only low oxides and metals, but also 
solid solutions are formed in the system. The following are the reactions of iron 
oxides with gaseous reducing agents: 

---