Universum: технические науки

Examples 
Example 1: "Biscuit Box" 
The “Biscuit Box” is made of an alloy of silver 
(main) and copper with traces of impurities. The boxes 
had to be cleaned because they were blackish. Two XRF 
spectra were captured, one before and one after cleaning 
with “flurin”. XRF spectra had two tasks: the thickness 
of the tarnishing layer and the composition of the layers, 
which had to instrumentally decide whether it was nec-
essary to clean and clean it well or not. The composition 
has been divided into two layers: tarnishing and alloy.
The depth of the surface analysis was about 15 μm, 
considering the K and L lines of silver. The average ap-
proximation error was 12% for the analyzed spectrum. 
Taking into account the estimated thickness of the upper 
layer of 0.01 μm, as well as its density, an error of 0.01 
7/15 11.5 = 0.05% was needed and not 12%. As can be 
seen on the spectrum plot: the XRF spectra before and 
after cleaning practically do not differ (Figure 3).
Figure 3. Two experimental XRF spectra, one before and one after cleaning. Sulfur peak is 118 channel,
chlorine peak is 134 channel. The two high peaks are the L line of silver 
It is necessary to take more than 20 sec so that the 
spectrum becomes even, and not a herringbone. If we 
capture the spectrum not only for 20 sec, but much more, 
for example, 999 sec, the spectrum will rise up and become 
a smoother curve. The spectrum is simply a histogram 
of the registered impulses distributed over energies. 

---

№ 10 (91)
октябрь, 2021 г. 
70 
We tested this statement on another XRF, Hitachi X-MET. 
We captured two spectra for 30 sec and for 600 sec, and 
compared them. Unfortunately for Hitachi there is no pub-
lished calibration file for PiMca to use yet. When and if 
the calibration file becomes available it may be possible 
with the help of Hitachi to determine even the ratio of the 
content of radium to thorium and thereby establish the age 
of metal artifacts [16].