1.4.1 Temperature program for coextrusion 
There are limits for setting the stretching temperatures of the MDO since the 
film will stick to the chromium-plated rolls. The sticking point for PP homopolymer is 
at approx. 140 – 145°C. For PP copolymer, it is approximately 120 - 125°C. 
Consequently, a plain film can be stretched at temperatures of 140 – 145°C, while a 
co-extruded film with PP copolymer as outside layers must be oriented at temperatures 
of 120 – 125°C. The required lower stretching temperatures for a co-extruded film 
would result in an increased thermal shrinkage and impaired sealing properties. 
To be able to stretch the PP homopolymer in the inner layer at higher 
temperatures than 120 – 125°C, the Teflon-coated pre-heating rolls are used. 
Considerably higher temperatures can be adjusted for the Teflon-coated rolls without 
making the film stick. Experience has shown that for coextruded film temperatures up 
to 134°C can be set for Teflon-coated rolls. 
Thus, also the film core can be heated up to 132°C. For the ensuing stretching 
process, however, chromium-plated rolls are necessary. For the process, the outside 
layers of the film must be cooled down again to 120 – 125°C. 
Since the radii of the stretch rolls are considerably smaller than the radii of the 
pre-heating rolls and therefore the residence time of the film on these rolls is shorter, 
only the outside layers of the film are cooled. 
By overheating the sealing layer on the Teflon-coated pre-heating rolls and by 
subsequent cooling down of the outside layers on the cooling rolls, it is possible to 

---

86 
orient the coextruded film at optimum temperatures for each layer, i.e. approximately 
120°C for the sealing layer and approximately 132°C for the core layer. 
1.4.2 Pre-heating rolls 
The preheating section heats the base web to just below the sticking point of 
the copolymer. The latter rollers are Teflon-coated to reduce sticking. Crystallinity is 
not alerted at this temperature but stretching is made easier.