Composite material, 2024-T3 aluminum sheet, AZ31 magnesium sheet, tensile tests, epoxy resin. 
Conclusions 
Within the scope of this study, FMLs with 3/2 stack order were produced by reinforcing carbon fibers with epoxy 
resin between 0.8 mm thick 2024-T3 aluminum and AZ31 magnesium plates. As a result of the experiments, the results 
shown below were obtained. 

Sanding and shot peening processes applied to improve the adhesive properties of metal sheets made the 
surfaces rough enough for lamination. It has been found that shot peening is more successful than sanding 
in this regard. 

With the effect of shot peening applied to metals, the tensile strength of AZ31 magnesium plate, whose both 
surfaces are treated, increased by 30%, and the tensile strength of 2024-T3 aluminum plate increased by 
15%. The main reason for this increase in strength is thought to be the deformation hardening of metals and 
permanent compressive stresses on the surfaces due to shot peening. 
References 
1.
Saleh, H. E, Koller, M.: Characterizations of Some Composite Materials. BoD – Books On Demand, 166, (2019). 
2.
Hahn, H. T, Tsai, S. W.: Introduction to Composite Materials. CRC Press, 486, (1980). 
3.
M.B.Babanli, 
N.A.Gurbanov 
and 
Y.A.Turen.: 
Metal 
matrix 
hybrid 
laminated 
composite 
materials. 
Equipment.Technologies.Materials,Vol 01, Issue 03 20, pp.74-78 (2020). 
5.
Benedict.A.V.: An Experimental Investigation of GLARE and Restructured Fiber Metal Laminates. (2012). 
M.B.Babanli
1 [0000-0003-1939-6511]
and Y.A.Tanriverdiyev
2[0000-0003-4108-4522]. 

---

6.
Kashfi M, Majzoobi G H, Bonora N, Iannitti G, Ruggiero A and Khademi E.: A new overall nonlinear damage model for 
fiber metal laminates based on continuum damage mechanics. Engineering Fracture Mechanics, 206, pp.21–33, (2019). doi: 
10.1016/j.engfracmech.2018.11.043 
7.
Fattal, D. S. A, Rabii, and Sudani, I. M. A.: Study the effect of shot peening with anodizing process on the mechanical 
properties and fatigue life of aluminum alloy 2024-T3. Advances In Natural And Applied Sciences, 10 (15), pp.43–52 (2016). 
8.
Jamalian, M. and Field, D. P.: Effects of shot peening parameters on gradient microstructure and mechanical properties of 
TRC AZ31. Materials Characterization, 148, pp.9–16, (2019). doi: 10.1016/j.matchar.2018.12.001 
9.
Wan, Y., Wang, Z.-Q., Zhou, L.-M., and Chang, M.-Z.: Tensile Test Performance of Fibre Reinforced SMATed Aluminium 
Laminates, Atlantis Press, pp.943–947, (2014). doi: 10.2991/icmsa-15.2015.175