Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

 
 
3.1.3.2  Soil organic acids leaching 
The  leaching  experiments  included  five  approaches  at  which  each  slag  was  submitted  to 
leaching  tests  with:  i)  humic  acid  at  pH  (4.4),  ii)  fulvic  acid  at  pH  (4.4),  iii)  artificial  root 
exudates solution at pH (4.4), iv) artificial root exudates solution at pH (2.9) and v) ultrapure 
water.  A  mass  of  3  g  of  each  slag,  crushed  to  size  fraction  below  0.3  mm,  was  placed  into 
batches  and  30  mL  of  leaching  solutions  were  added  to  maintain  liquid  to  solid  ratio  of  10. 
Independent batches in triplicates were accompanied by procedural blanks. The batches were 
wrapped up in aluminium paper in order to avoid photo-oxidation of organic compounds, kept 
at  ambient  temperature  (21±1°C)  on  a  table  shaker  continuously  agitated  at  150  rpm. 
Leaching solutions with slags were left at free pH drift. The leachates were sampled after 24, 
48,  72,  168  and  960  hours.  At  each  sampling  time,  the  pH  of  the  leaching  solution  was 

---

CHAPTER 3: MATERIALS AND METHODS
 
 
91 
 
measured,  solutions  were  filtered  using  0.45  µm  nitrocellulose  filters  (Whatman), 
immediately  acidified  using  suprapure  HNO
3 
(2%  v/v)  to  prevent  precipitate  formation  and 
stored at 4°C until analysis.