Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-water jacket 
furnace slag 
 
FeO: 27% 
(Fe: 21%) 
Cu: 0.2% 
Co: 1.7% 
Zn: 5% 
PbO: 0.9% 
(Pb: 0.8%) 
Extractant: HNO
3 
and ammonia 
FS: <212 µm 
L/S: 10 
LT: 2 – 20 h 
T: 25 – 80°C 
AS: 500 rpm 

 
Extraction of original  sample (25°C, pH=0, LT: 20 h, Cu 46% (0.9 g/kg), Co 
95% (16.2 g/kg), Zn 86% (43 g/kg), Pb 92% (7.7 g/kg), Fe 79% (165.8 g/kg)) 

  Cold-water-quenching slag (25°C, pH =12, LT: 20 h, Cu 90% (1.8 g/kg) #, Co 
(0.2  g/kg),  Zn  (0.5  g/kg),  Pb  (0.1  g/kg),  Fe  (2.1  g/kg)  <  1%)  shows  good 
selectivity in leaching at high alkaline conditions 

  Air-cooled slag (25°C, pH=12, LT: 20 h Cu, Co, Zn, Pb 22-36%, Fe 5%) 

  Slow-cooled slag (T: 25 – 80°C, pH=12, LT: 20 h, extraction <2%) was found 
to prevent metal extraction 

  Increase of temperature is favorable for metal extraction 

  Water-granulated slag is found as useful material if recovery intended 
Tshiongo et 
al. (2010)