Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-converter slag 
 
Fe: 52% 
Cu: 2.6% 
Zn: 0.43% 
Co: 0.36% 
Ni: 0.05% 
 
Roasting agent: Fe
2
(SO
4
)
3
 × H
2
O 
Fe
2
(SO
4
)
3
 × H
2
O /slag ratio: 1 
Roasting T: 300 – 800°C 
Roasting time: 0.5 – 4 h 
Extractant: H
2
O and H
2
SO
4
 
FS: < 74µm 
L/S: 5 (20% of solid) 
T: 25°C 
LT: 0.5 h  
AS: present (n.i. rpm) 

  Metals  recovery  increases  with  increased  roasting  temperature  to  500-550°C 
reaching  Cu> 95% (24.7 g/kg) #, Zn 65% (2.8 g/kg), Co 40% (1.4 g/kg), Ni< 
15% (0.08 g/kg) (0.5 h leaching) 

  Roasting  time  of  2  h  was  found  to  give  the  best  values  of  extracted  metals 
during 0.5 h leaching 

  Increase  of  ferric  sulfate/slag  ratio  improves  Cu  extraction  (Cu~75%  (~19.5 
g/kg) at 0.5 ratio, Cu> 95% (24.7 g/kg) # at 1-2.5 ratio 
Altundoǧan  
and Tümen 
(1997)