Copper metallurgical slags: mineralogy, bio/weathering processes and metal bioleaching

Cu-converter slag 
 
Fe: 38.32% 
Cu: 4.03% 
Co: 0.48% 
Ni: 1.98% 
 
Roasting/leaching 
Roasting agent : (NH
4
)
2
SO
4 
(0.5 – 2.5 × 
stoichiometric) 
Roasting T: 200 – 600°C 
Roasting time: 0.25 – 2 h 
Extractant: H
2
O  
FS: 60 – 300 µm 
 

 
Increase of roasting temperature from 200 to 400°C increased recovery of Cu, 
Ni, Fe, whereas Co extraction was not affected by temperature 

  The time of 1 h was found to be suitable roasting duration 

  Increasing amount of (NH
4
)
2
SO
4 
improves metal extraction 

 
Optimal sulfation temperature is 400°C 

  Reduction of particle size  has positive effect on  metals recovery, especially in 
the range 300-75 µm 

 
Optimal conditions: FS < 75µm, 2.5×stoichiometric requirement of (NH
4
)
2
SO
4, 
T: 400°C, LT: 1 h (Co 85% (4.1 g/kg), Ni 80% (15.8 g/kg), Cu 85% (34.3 g/kg) 
#, Fe 37% (141.8 g/kg)) 
Sukla et al., 
(1986) 

---