Asian Research Journals

Figure 3. Results of X-ray diffraction analysis of burnt samples at 125°C - 750°C 
As shown in the diffractogram in the figure above, ZnO samples burnt at different temperatures 
have peaks characteristic for the structure of zinc oxide in the crystal structure. In addition, as the 
temperature  of  the  crease  increases,  the  peak  intensity  is  explained  by  the  particle  aggregation 
and the breakdown of the gel structure. Next, we investigated the  IR spectrum of zinc oxide in 
the nanoscale from 125°C to 750°C. Analysis of the IR spectra of the dried zinc oxide sample at 
125°C  shows  that  the  sample  contains  hydroxyl  1020-1067  cm
-1
  absorption  area  and  acetate 
group  corresponding  to  the  absorption  domain  725,  1332,  1400,  1550,  2880-2970  cm
-1
. 
Chemically and physically adsorbed water (677, 877, 918, 1550, 3145-3425 cm-1), amino group 
(677, 877, 1550 cm
-1
) and Zn(H
2
O)
2
2+
 and Zn (NH
3
)
 2
2+
 groups also available. 
Further analysis of the IK spectrum showed changes in valence vibrations (2800-3900 cm
-1
) and 
deformation oscillations (4000-900 cm
-1
) in the IR spectra with increasing sample temperature. 
In the IR spectra of nanoscale ZnO samples heated at 400-750°C, only the maximum apparent at 
450 cm
-1
 is observed. This is due to the Zn-O bond vibration in the spectrum. 

---

ISSN: 2278-4853           Special Issue, March, 2020     Impact Factor: SJIF 2020 = 6.882 
TRANS