Production  of  Fe-modified  bentonite  by  Zol-gel  method: 

Aqueous  suspension  of  bentonite 

(ratio of solid and liquid phases 1:10, aqueous extract of the suspension pH i 8) was left for one 

day to swell at room temperature. It was then treated with ultrasound at a frequency of 22 Gts for 

good dispersion of the bentonite particles for 3 min. The intercalating solution was prepared by 

mixing 1.0 M solutions of iron (III) chloride and sodium hydroxide. ([OH

-

]/[Fe

3+

]=2,0) and left 

at  room  temperature  for  one  day.  The  sol  obtained  after  ageing  was  added  dropwise  to  a  10% 

aqueous suspension of bentonite. The resulting modified bentonite was separated from the liquid 

phase in a Büchner funnel using a vacuum pump after 24 h. It was washed with distilled water 

until a negative reaction to the chloride ions and dried at room temperature. It was then thermally 

treated at 500 

℃

 for 2 h.