wooden capillaries due to the difference in temperature of hot-cold baths, which in turn plays a 

key role in the adopted method of dipping. 

3. ANALYSIS OF EXPERIMENTS

.

 

Analysis  of  the  results  shows  that  the  degree  of  absorption  of  sulfur  solution  in  wood  has  the 

greatest effect on the duration of soaking wood in a cold bath. The minus (-) signs in front of the 

coefficients are directly  proportional to the rate of sulfur absorption for factors X1 and X2, the 

rate  of  heating  of  the  wood  in  a  hot  bath,  and  the  rate  of  cooling  of  the  solution  to  the 

temperature  of  the  cold  bath.  This  confirms  the  theoretical  research  on  the  impregnation  of 

porous materials in solution. 

According to the results obtained, the parameters of the optimal mode of the process of soaking 

wood in a solution of sulfur in a hot-cold bath are as follows: 

- Duration of heating wood in a hot bath - 30-35 minutes; 

- Cooling time of the solution - 5-10 minutes; 

- Duration of soaking in a cold bath - 80 - 90 min. 

Let's compare the optimal mode of spraying terracotta with other deciduous trees. To do this, we 

take a mountain whose anatomical structure, that is, its micro- and macrostructure, is close to it. 

For comparison, we accept the process of soaking the sheets in a solution of sulfur. 

Here,  too,  this  process  is  carried  out  by  the  method  of  hot-cold  baths,  the  results  of  which  are 

performed graphically and are shown in Figure 1. 

The temperature-time soaking mode of the compared variants consists of the following sections. 

(Figure 1.) 

аb, а

1

b

1 

–

 the area ofa sharp drop in temperature as a result of bathing wood in a hot bath; 

Bс, с1d1

- 

wood soaking area in a hot bath: 

сd, d

1

h

1- 

- temperature difference of sulfur solution; 

DH, h1e1

 -

- a plot of soaking wood in a cold bath 

b

1

с

1-

 the site of heating the sulfur solution to the initial temperature of the hot bath;