An abstract of the thesis of


Table 2.1: Average values, confidence interval of 1/D



Download 5,25 Mb.
Pdf ko'rish
bet12/53
Sana25.02.2022
Hajmi5,25 Mb.
#464341
1   ...   8   9   10   11   12   13   14   15   ...   53
Bog'liq
Edward Le PhD Dissertation

Table 2.1: Average values, confidence interval of 1/D
t
 for PF resin and PVA based wood glue of normal and VTC strands 
 
(1/
D
t
) in mm/MPa 
PF resin 
PVA Based 
Adhesive Coverage 
VTC 
95%* 
NS** Normal Strand 
95%* 
NS** Normal Strand 
95%* 
NS** 
1% 
0.01177 
± 0.00640 
20 
0.01628 
± 0.01406 
22 
0.14645 
± 0.05617 
17 
25% 
0.00210 
± 0.00343 
20 
0.01048 
± 0.00995 
22 
0.06536 
± 0.01832 
16 
100% 
-0.00017 ± 0.00032 
20 
-0.00022 
± 0.00042 
22 
0.03693 
± 0.01963 
15 
* 95% Confidence interval 
** Number of DLS sample 


26 
0
0.03
0.06
0.09
0.12
0.15
0.18
0.21
PVA Adhesive Coverage
1
/D
t
(m
m
/M
P
a
)
1% 25% 100%
Unmodified (Normal) Strand
Figure 2.5. Measured adhesive compliance for PVA resin on normal (unmodified) strands 
for different percent of adhesive coverage. 
For better comparison Figure 2.7 plots 1/
D
t
as the function of adhesive coverage 
for both PF resins and PVA wood glue. The PVA wood glue has much lower 
D
t
than PF 
resins. At 100% coverage, the PVA glue bond, unlike PF glue bonds, did not perform as 
an interphase being reinforced by resin. The relative error bars for PVA were slightly 
better than for PF due to the larger magnitude of 1/
D
t
, which resulted in larger 
displacements caused by glue-line deformation. 


27 
-0.005
0
0.005
0.01
0.015
0.02
0.025
0.03
0.035

Download 5,25 Mb.

Do'stlaringiz bilan baham:
1   ...   8   9   10   11   12   13   14   15   ...   53




Ma'lumotlar bazasi mualliflik huquqi bilan himoyalangan ©hozir.org 2024
ma'muriyatiga murojaat qiling

kiriting | ro'yxatdan o'tish
    Bosh sahifa
юртда тантана
Боғда битган
Бугун юртда
Эшитганлар жилманглар
Эшитмадим деманглар
битган бодомлар
Yangiariq tumani
qitish marakazi
Raqamli texnologiyalar
ilishida muhokamadan
tasdiqqa tavsiya
tavsiya etilgan
iqtisodiyot kafedrasi
steiermarkischen landesregierung
asarlaringizni yuboring
o'zingizning asarlaringizni
Iltimos faqat
faqat o'zingizning
steierm rkischen
landesregierung fachabteilung
rkischen landesregierung
hamshira loyihasi
loyihasi mavsum
faolyatining oqibatlari
asosiy adabiyotlar
fakulteti ahborot
ahborot havfsizligi
havfsizligi kafedrasi
fanidan bo’yicha
fakulteti iqtisodiyot
boshqaruv fakulteti
chiqarishda boshqaruv
ishlab chiqarishda
iqtisodiyot fakultet
multiservis tarmoqlari
fanidan asosiy
Uzbek fanidan
mavzulari potok
asosidagi multiservis
'aliyyil a'ziym
billahil 'aliyyil
illaa billahil
quvvata illaa
falah' deganida
Kompyuter savodxonligi
bo’yicha mustaqil
'alal falah'
Hayya 'alal
'alas soloh
Hayya 'alas
mavsum boyicha


yuklab olish