Fig. 1.24. Effect of alkali content on accelerated 
strength
1.75 
The influence of the alkalis on strength is 
complicated by the fact that they may be incorporated 
into the calcium silicate hydrates or may 
exist as soluble sulfates; their action in the two 
cases is not the same. K2O is believed to replace 
one molecule of CaO in C2S with a consequent 
rise in the C3S content above that calculated.
1.6 
However, we can say that, generally, the alkalis 
increase the early strength development and reduce 
the long-term strength.
1.79 
Osbæck
1.95 
confirmed 
that a higher alkali content in Portland cement 
increases the early strength and decreases 
the long-term strength. 
The alkalis are known to react with the socalled 
alkali-reactive aggregates (see p. 
144
), and 
cements used under such circumstances often 
have their alkali content limited to 0.6 per cent 
(measured as equivalent Na2O). Such cements 
are referred to as 
low-alkali cements
. 
One other consequence of the presence of alkalis 
in cement should be mentioned. Fresh Portland 
cement paste has a very high alkalinity (pH 
above 12.5) but, in a cement with a high alkali 
content, the pH is even higher. In consequence, 
human skin is attacked and dermatitis or burns 

---

166 
may result; eyes can also be injured. For this reason, 
the use of protective clothing is essential. 
We can see then that the alkalis are an important 
constituent of cement, but full information 
on their role is yet to be obtained. It may be 
noted that the use of pre-heaters in modern dryprocess 
cement plants has led to an increase in 
the alkali content of cement made from given raw 
materials. The alkali content, therefore, has to 
be controlled, but limiting the alkali content too 
severely results in an increased energy consumption. 
1,76 A more efficient dust collection also increases 
the alkali content of the cement when the 
dust is re-incorporated into the cement because 
the dust contains a large amount of alkalis; this 
may be as high as 15 per cent, in which case the 
dust, or some of it, has to be discarded.