1.6.3 Flame treatment 
The flame treatment has the same function as corona treatment. 
Flaming consists of exposing the surface to be decorated to a suitable oxidizing 
flame for a period in the range of 0,2 to 3,0 seconds. This treatment brings about a 
change to the polymer surface that makes it wettable and permits a strong adhesive 
bond between the film surface and the coating. This change in surface properties can 
be readily seen by immersing an untreated and treated film in water. 
On removal, the water will run off in globules from the untreated surface but 
will form a continuous film on the treated surface which will last for a varying length 
of time depending on the present flaming conditions used. 
The following major parameters should be monitored for effective flaming 
conditions: 
−
Gas/air ratio: it depends on the type of gas used (town gas, methane, propane, and 
butane are suitable). A laminar flow flame is preferable to the turbulent flame. 

---

93 
−
The distance of the burner to the film surface. 
−
The residence time of the film in the flame. 
It has been established that the gas/air ratio is the most important and critical 
factor in flame treatment. The importance of control over this parameter cannot be 
overstressed and the gas/air flow must be maintained at a pre-determined level. 
The effect of incorporating antistatic additives depends on the type of additive 
used, its concentration, and the type of flame treater. Additives, which by their 
diffusivity and compatibility characteristics, become active immediately after 
processing, demand more critical flaming conditions, and can give rise to difficulty if 
used at higher concentrations than those recommended. The level of addition at which 
difficulty is encountered in achieving acceptable print adhesion dependents on the type 
of burner used for treatment. Most anti-static additives are only effective after flaming, 
and these additives do not affect on the flaming conditions necessary for acceptable 
print adhesion.