8. Mechanical Characteristics 
 
8.1 Drop Test 
Test method: Cell(as of shipment or full charged) drop onto the oak-board 
(thickness: 

30mm) from 1.5m height at a random direction 6 times. 
Criteria: No leakage 
8.2 Vibration Test 
Test method: Cell(as of shipment) is vibrated along 2 mutually 
perpendicular axes with total excursion of 1.6mm and with
frequency cycling between 10Hz and 55Hz by 1Hz/min.
Criteria: No leakage
Charge temperature 
Discharge temperature
0

25

45

Relative Capacity 
80% 
100% 
100% 
25



SAMSUNG SDI Confidential Proprietary

Spec. No. 
ICR18650-22F 
Version No.
Tentative 
Samsung SDI., Energy Business Division. 
5
9. Safety 
 
10.1 Overcharge Test
Test method: To charge the standard charged cell with 12V and 2200mA at 25

for 2.5 hours. 
Criteria: No fire, and no explosion. 
10.2 External Short-circuit Test 
Test method: To short-circuit the standard charged cell by connecting positive and
negative terminal by less than 50m
Ω
wire for 3 hours. 
Criteria: No fire, and no explosion. 
10.3 Reverse Charge Test 
Test method: To charge reversely the standard charged cell with charge current 
2200mA for 2.5 hours.
Criteria: No fire, and no explosion. 
10.4 Heating Test 
Test method: To heat the standard charged cell at heating rate of 5

per minute up to 
130

and keep the cell in oven for 60 minutes. 
Criteria: No fire, and no explosion. 
 
 
10. Warranty 
Samsung SDI will be responsible for replacing the cell against defects or poor 
workmanship
for 1year from the date of shipping. Any other problems caused by malfunction of the
equipment or unsuitable use of the cell are not under this warranty. 
The warranty set forth in proper use, handling conditions described above,
and excludes in the case of a defect which is not related to manufacturing of the cell.

Download 213,27 Kb.

Do'stlaringiz bilan baham:
1   2   3   4   5   6   7   8   9   10   11




Ma'lumotlar bazasi mualliflik huquqi bilan himoyalangan ©hozir.org 2024
ma'muriyatiga murojaat qiling

kiriting | ro'yxatdan o'tish
    Bosh sahifa
юртда тантана
Боғда битган
Бугун юртда
Эшитганлар жилманглар
Эшитмадим деманглар
битган бодомлар
Yangiariq tumani
qitish marakazi
Raqamli texnologiyalar
ilishida muhokamadan
tasdiqqa tavsiya
tavsiya etilgan
iqtisodiyot kafedrasi
steiermarkischen landesregierung
asarlaringizni yuboring
o'zingizning asarlaringizni
Iltimos faqat
faqat o'zingizning
steierm rkischen
landesregierung fachabteilung
rkischen landesregierung
hamshira loyihasi
loyihasi mavsum
faolyatining oqibatlari
asosiy adabiyotlar
fakulteti ahborot
ahborot havfsizligi
havfsizligi kafedrasi
fanidan bo’yicha
fakulteti iqtisodiyot
boshqaruv fakulteti
chiqarishda boshqaruv
ishlab chiqarishda
iqtisodiyot fakultet
multiservis tarmoqlari
fanidan asosiy
Uzbek fanidan
mavzulari potok
asosidagi multiservis
'aliyyil a'ziym
billahil 'aliyyil
illaa billahil
quvvata illaa
falah' deganida
Kompyuter savodxonligi
bo’yicha mustaqil
'alal falah'
Hayya 'alal
'alas soloh
Hayya 'alas
mavsum boyicha


yuklab olish