Mechanical Characterization of Solid Oxide Fuel Cells and Sealants

Appendix
.
By plotting the deformation rate as a function of the applied loading force and temperature, the 
stress exponent and activation energy can be obtained, see 
Figure
 5-18
. The values of ln(
H
) were 
determined from the intersection on Y-axis of 
Figure
 5-18
 
(a)
, which were used to determine A 
values (see 
Appendix
). The obtained creep parameters from the 4-point bending are shown in 
Table
 5-6
.  
4-point bending creep yielded an average stress exponent 1.4 ± 0.1, which is similar to the value 
obtained from ring-on-ring bending creep. This indicates diffusion-dominated creep. The average 
activation energy of 147 ± 1 kJ/mol for the temperature range of 800°C and 900°C is similar to 
the value of 177 kJ/mol obtained from ring-on-ring creep for a stress of 10 MPa

---

Results and discussion 
95 
a)
b)
Figure 5-18: Stationary deformation rates are plotted as a function of (a) applied loading force; 
(b) inverse temperatures.

---

Results and discussion 
96 
Table 5-6: The creep parameters of material C obtained from 4-point bending test. 
Temperature (°C) 
A 
(s
-1 
MPa
-n
) 
Stress exponent, 
n
Activation energy 
Q,
(KJ/mol) 
800 
900 
5.7 × 10
-4 
3.3 × 10
-4 
1.3 
1.5 
- 
- 
800 - 900 
- 
147 ± 1 
5.1.3.4.
Discussion
5.1.3.4.1.
Activation energies 
The activation energies obtained from the different tests for the temperature range of 800 °C to 
900 °C are summarized in Table